MIM Common Material List
| Material Group | Material Grade | Standards | Min. Density(g/cm) | Min. Yield Strength,Rpo.2 (MPa [KSI]) | Min. UltimateTensile Strength(MPa [KSI]) | Min.Elongation % | Hardness |
| Low Alloy | 100Cr6 (as sintered) | DIN 1.3505;AISI E52100;UNS G52986 | 7,5 | 500 [72.5] | 900 [130.5] | 5 | 230-290 HV10 |
| 100Cr6 (heat treated) | 7,5 | ≥60 HRC | |||||
| FN02 (as sintered) | MPIF MIM-2200 | 7,5 | 150 [21.7] | 260 [37.7] | 25 | 90-110 HV10 | |
| FN02 (case hardened) | 7,5 | ≥55 HRC | |||||
| FN0205 (as sintered) | 7,5 | 170 [24.6] | 380 [55] | 3 | 100-150 HV10 | ||
| FN0205 (heat treated) | 7,5 | 700 [101.5] | 800 [116] | 5 | 30 HRC | ||
| FN0205 (heat treated) | 7,5 | 1000 [145] | 1200 [174] | 2 | 55 HRC | ||
| FN08 (as sintered) | MPIF/ASTM MIM-2700 | 7,5 | 210 [30.5] | 380 [55] | 15 | 90-140 HV10 | |
| FN08 (case hardened) | 7,5 | ≥55 HRC | |||||
| 4605 (as sintered) | MPIF/ASTM MIM-4605 | 7,55 | 400 [58] | 600 [87] | 5 | ≥150 HV10 | |
| 4605 (heat treated) | 7,55 | 1100 [159.5] | 1300[188.5] | 5 | ≥40 HRC | ||
| 4605 (heat treated) | 7,55 | 1500 [217.6] | 1900 [275.6] | 2 | ≥55 HRC | ||
| 8620 (as sintered) | DIN 1.6523; AISI/SAE 8620;UNS G86200 | 7,4 | 400 [58] | 650 [94.3] | 3 | 190-230 HV10 | |
| 8620 (heat treated) | 7.4 | ≥60 HRC | |||||
| 8620 (carbonitrided) | 7,4 | ≥64 HRC | |||||
| 8740 (as sintered) | DIN 1.6546;AISI/SAE 8740;UNS G87400 | 7,5 | 530 [76.9] | 860 [124.7] | 8 | 190-210 HV10 | |
| 8740 (heat treated) | 7,5 | 1400 [203] | 1600 [232] | 5 | ≥53 HRC | ||
| 42CrMo4 (as sintered) | DIN 1.7225; AISI/SAE 4140;UNS G41400 | 7,4 | 400 [58] | 650 [94.3] | 3 | 130-230 HV10 | |
| 42CrMo4 (heat treated) | 7,4 | 1250[181.3] | 1450 [210.3] | 2 | ≥45 HRC | ||
| 1010 (as sintered) | AISI 1010 | 7,5 | 230 [33.4] | 400 [58] | 26 | ||
| 1010 (heat treated) | 7,5 | 60 HRC | |||||
| Stainless Steel | 316LA | DIN 1.4404; AISI 316L; UNS S31603 |
7,75 | 180[26.1] | 510 [74] | 50 | 120 HV10 |
| 316L (all others) | 7.9 | 180[26.1] | 510 [74] | 50 | 120 HV10 | ||
| 17-4 PH (as sintered) | Din 4.4542; AISUNSS174000; SAE J 467 | 7,6 | 660 [95.71 | 950 [137.8] | 3 | 32 HRC | |
| 17-4PH (H900) | 7,6 | 950 [137.8] | 1100 | 5 | 40 HRC | ||
| 310N (N sintered) | Nb-modified DIN 1.4848: UNS 94203 |
7,72 | 450[65.31 | 800 [116] | 16 | 235 HV10 | |
| 310N (Ar sintered) | 7,65 | 250 [36.31 | 600 [87] | 40 | 160 HV10 | ||
| 420W (as sintered) | Nb-modified DIN 1.4028;UNSS42020;UNS J91154;AISI420F | 7,6 | 650 [94.3] | 800 [116] | 0,97 | ≥55 HRC | |
| 420W (heat treated) | 7,6 | 1560 [226.3] | 0,85 | ≥61 HRC | |||
| PANACEA | 7,5 | 690[100.1] | 1090[158.1] | 35 | 28-32 HRC | ||
| Heat Resistant | GHS-4 | 7,9 | 600 [87] | 800 [116] | 2 | 33-37 HRC | |
| Titanium | Ti | DIN 3.7056:Commercially Pure; ASTM Grade 4;UNS R50700 | 4,2 | 480 [69.6] | 550 [79.8] | 5 | 160-240 HV10 |